| Speciality Boards |
| |
Graphic - Art Maestro(C2s)
|
|
Art Maestro
is a higher weight coated card developed on a high whiteness
base with even smoothness and gloss. Its stiffness is measurably
superior to conventionally made C2S boards.
|
|
| |
| Specifications |
| |
| SUBSTANCE
(GSM)TAPPI T
410 om - 98
|
CALIPER (UM)
TAPPI T 411 om-97
|
BENDING
RESISTANCE (L&W)Mn
TAPPI T 556 pm - 95
|
200 |
190 |
Md |
CD |
GM |
210 |
200 |
50 |
21 |
32 |
220 |
210 |
53 |
25 |
36 |
230 |
220 |
58 |
28 |
40 |
250 |
240 |
65 |
31 |
45 |
260 |
250 |
80 |
38 |
55 |
270 |
260 |
87 |
41 |
60 |
| |
|
280 |
48 |
69 |
285 |
270 |
110 |
53 |
76 |
300 |
285 |
120 |
58 |
83 |
330 |
315 |
138 |
66 |
95 |
350 |
335 |
174 |
83 |
120 |
400 |
385 |
188 |
90 |
130 |
| |
|
300 |
160 |
219 |
Tol: +-3% |
+- 5% |
+ - 10% |
|
| |
| Substanceless than 220 GSM are
without back coating unless specified. |
| |
|
| |
| PARAMETER
|
UNITS
|
VALUEpm
- 95
|
PLY
BOND
TAPPI T- 833 pm-94 |
J/
M2 |
Md |
SMOOTHNESS (PPS)
BACK
ISO 8791 - 2 |
MICRONS |
<1.8
<2.0 |
BRIGHTNESS
ISO
TOP
BACK
ISO 2469 |
% |
93+-
1.0
93+- 1.0 |
SURFACE STRENGTH (IGT)
IGT (MED. VISCOSITY)
ISO 3782 |
M/S |
>0.7 |
GLOSS
AT 750
TAPPI 480 om - 92 |
% |
>60 |
WHITENESS
TOP
BACK |
% |
116+- 1.0
116+- 2.0 |
MOISTURE
CONTENT
<250 GSM
250-300 GSM
>300 GSM
TAPPI T 412 om - 94 |
% |
6.5- 7.5
7.0-8.5
7.0 - 9.0
|
|
| |
| Note |
| |
- Tolerances are based upon 95% confidence limit on single
mill measurment of random samples
- Specifications are subject to change without any prior
notice.
|
| |
| Variants |
| |
- Range 200 - 260, 300, 330, 350 gsm .
|
| |
| Features |
| |
- Suitable for offset, letterpress, gravure, flexo and screen
printing.
- Suitable for embossing and foil stamping.
- End uses:Greeting Cards,Visiting Cards, Wedding Cards,Brochures,
Pamphlets, Tags, POPs etc.
|
| |
| Uses |
| |
- Greeting cards, Post Cards, Invitations,
- Menu Cards Publication & Book covers, Directories
- Promotional Folders & Catalogs
- Posters & Danglers (POP)
- Brochures
- Tags & Inserts
- Folders
- Flyers & Mailers
|
| |